PA66 AFR450X2 阻燃,玻璃纤维增强

添加时间:2013-05-16  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

Eurostar Engineering Plastics
STARFLAM(阻燃)(PA-PP)


Starflam* PA66 AFR450X2
产品描述:Starflam PA66 AFR450X2 是一个含有阻燃剂和玻璃纤维增强的聚酰胺66树脂注塑成型。
Description:Starflam AFR450X2 is a Red Phosphorous Flame Retardant, Glass Fiber Reinforced Polyamide 66 Injection Molding Resin


产品数据表

功能 PROPERTY (1) UNIT STANDARD VALUE
MECHANICAL Flexural Modulus,2 mm/min MPa ISO 178 8000
Flexural Stress,break,2 mm/min MPa ISO 178 210
Hardness,Rockwell L - ISO 2039-2 108
Tensile Modulus,1 mm/min MPa ISO 527 8700
Tensile Strain,break,5 mm/min % ISO 527 2
Tensile Stress,break,5 mm/min MPa ISO 527 160
IMPACT Izod Impact,notched 80*10*4 +23℃ kJ/m^2 ISO 180/1A 12
Izod Impact,notched 80*10*4 -20℃ kJ/m^2 ISO 180/1A 9
Izod Impact,notched 80*10*4 -40℃ kJ/m^2 ISO 180/1A 8
THERMAL Ball Pressure Test,125℃ +/- 2℃ - IEC 60695-10-2 PASSES
CTE,23℃ to 60℃,flow 1/℃ ISO 11359-2 2.80E-05
CTE,23℃ to 60℃,xflow 1/℃ ISO 11359-2 9.00E-05
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm ISO 75/Ae 248
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm ISO 75/Be 250
Relative Temp Index,Elec UL 746B 110
Relative Temp Index,Mech w/impact UL 746B 110
Relative Temp Index,Mech w/o impact UL 746B 115
Vicat Softening Temp,Rate B/120 ISO 306 245
Vicat Softening Temp,Rate B/50 ISO 306 245
PHYSICAL Density g/cm^3 ISO 1183 1.33
Moisture Absorption (23℃/50% RH) % ISO 62 1.2
Mold Shrinkage on Tensile Bar,flow % E2P Method 0.3-0.5
Water Absorption,(23℃/sat) % ISO 62 6
FLAME CHARACTERISTICS Glow Wire Flammability Index 960℃,passes at mm IEC 60695-2-12 2
UL E2P measurement,94V-2 Flame Class Rating mm UL 94 by E2P 0.8
UL Recognized,94V-0 Flame Class Rating mm UL 94 1.7
ELECTRICAL Comparative Tracking Index V IEC 60112 600
Dielectric Strength,in oil,3.2 mm kV/mm IEC 60243-1 17
Dissipation Factor,1 MHz - IEC 60250 0.0119
Dissipation Factor,50/60 Hz - IEC 60250 0.0054
Relative Permittivity,1 MHz - IEC 60250 2.8
Relative Permittivity,50/60 Hz - IEC 60250 3
Surface Resistivity,ROA Ohm IEC 60093 >1.E+16
Volume Resistivity Ohm-cm IEC 60093 >1.E+15
PARAMETER Setting Unit
Drying Temperature 75-85
Drying Time 4-6 hrs
Maximum Moisture Content 0.1 %
Mold Temperature 60-90
Rear-Zone 1 Temperature 275-285
Middle-Zone 2 Temperature 275-285
Front-Zone 3 Temperature 275-285
Melt Temperature 275-285