添加时间:2013-05-16  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

Eurostar Engineering Plastics
STARFLAM(阻燃)(PA-PP)

 

Starflam* PA66 AFR200Y
产品描述:Starflam PA66 AFR200Y 是一个非填充式,无卤素和(红磷低至无)阻燃剂,尼龙66注塑树脂
Description:Starflam AFR200Y is Unfilled, Halogen Free and Red Phosphorous Free, Flame Retardant, Polyamide 66 Injection Molding Resin

 

产品数据表

功能 PROPERTY (1) UNIT STANDARD VALUE
MECHANICAL Flexural Modulus,2 mm/min MPa ISO 178 3300
Flexural Stress,yield,2 mm/min Mpa ISO 178 120
Hardness,Rockwell R - ISO 2039-2 118
Taber Abrasion,CS-17,1 kg mg/1000cy E2P Method 24
Tensile Modulus,1 mm/min MPa ISO 527 3400
Tensile Strain,break,5 mm/min % ISO 527 9
Tensile Strain,yield,5 mm/min MPa ISO 527 4.8
Tensile Stress,break,5 mm/min MPa ISO 527 78
Tensile Stress,yield,5 mm/min MPa ISO 527 80
IMPACT Charpy  23℃,Unnotch Edgew 80*10*4 sp=62mm kJ/m^2 ISO 179/1eU >100
Charpy  23℃,V-notch Edgew 80*10*4 sp=62mm kJ/m^2 ISO 179/1eA 3
Charpy -30℃,Unnotch Edgew 80*10*4 sp=62mm kJ/m^2 ISO 179/1eU 70
Charpy -30℃,V-notch Edgew 80*10*4 sp=62mm kJ/m^2 ISO 179/1eA 3
Izod Impact,notched 80*10*4 +23℃ kJ/m^2 ISO 180/1A 4
Izod Impact,notched 80*10*4 -20℃ kJ/m^2 ISO 180/1A 4
Izod Impact,notched 80*10*4 -30℃ kJ/m^2 ISO 180/1A 3
Izod Impact,notched 80*10*4 -40℃ kJ/m^2 ISO 180/1A 3
THERMAL Ball Pressure Test,125℃ +/- 2℃ - IEC 60695-10-2 PASSES
CTE,23℃ to 60℃,flow 1/℃ ISO 11359-2 8.50E-05
CTE,23℃ to 60℃,xflow 1/℃ ISO 11359-2 8.50E-05
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm ISO 75/Ae 90
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm ISO 75/Be 210
Relative Temp Index,Elec UL 746B 130
Relative Temp Index,Mech w/impact UL 746B 90
Relative Temp Index,Mech w/o impact UL 746B 115
Vicat Softening Temp,Rate B/120 ISO 306 245
Vicat Softening Temp,Rate B/50 ISO 306 247
PHYSICAL Density g/cm^3 ISO 1183 1.17
Moisture Absorption (23℃/50% RH) % ISO 62 1.1
Mold Shrinkage on Tensile Bar,flow % E2P Method 1.1-1.5
Water Absorption,(23℃/sat) % ISO 62 7.5
FLAME CHARACTERISTICS Glow Wire Flammability Index 960℃,passes at mm IEC 60695-2-12 1
Oxygen Index (LOI) % ISO 4589 29
UL Recognized,94V-0  Flame Class Rating mm UL 94 0.75
ELECTRICAL Comparative Tracking Index V IEC 60112 600
Comparative Tracking Index,M V IEC 60112 550
Dielectric Strength,in oil,3.2 mm kV/mm IEC 60243-1 15
Surface Resistivity,ROA Ohm IEC 60093 >1.E+15
Volume Resistivity Ohm-cm IEC 60093 >1.E+15
PARAMETER Setting Unit
Drying Temperature 75-85
Drying Time 4-6 hrs
Maximum Moisture Content 0.2 %
Mold Temperature 60-90
Rear-Zone 1 Temperature 260-270
Middle-Zone 2 Temperature 265-280
Front-Zone 3 Temperature 270-280
Melt Temperature 265-280