PA66 AFR200B 未填充,阻燃尼龙66

添加时间:2013-05-16  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

Eurostar Engineering Plastics

STARFLAM(阻燃)(PA-PP)
 
Starflam* PA66 AFR200B
产品描述:Starflam PA66 AFR200B 是一个未填充,阻燃尼龙66注塑树脂
Description:Starflam AFR200B is a Unfilled, Flame Retardant Polyamide 66 Injection Molding Resin
 
产品数据表
功能 PROPERTY (1) UNIT STANDARD VALUE
MECHANICAL Flexural Modulus,2 mm/min MPa ISO 178 2800
Flexural Stress,break,2 mm/min Mpa ISO 178 105
Hardness,Rockwell R - ISO 2039-2 120
Tensile Modulus,1 mm/min MPa ISO 527 3000
Tensile Strain,break,50 mm/min % ISO 527 6
Tensile Strain,yield,50 mm/min MPa ISO 527 3.7
Tensile Stress,break,50 mm/min MPa ISO 527 80
Tensile Stress,yield,50 mm/min MPa ISO 527 80
IMPACT Izod Impact,notched 80*10*4 +23℃ kJ/m^2 ISO 180/1A 5
Izod Impact,notched 80*10*4 -20℃ kJ/m^2 ISO 180/1A 4
zod Impact,notched 80*10*4 -40℃ kJ/m^2 ISO 180/1A 3
THERMAL Ball Pressure Test,125℃ +/- 2℃ - IEC 60695-10-2 PASSES
CTE,23℃ to 60℃,flow 1/℃ ISO 11359-2 8.50E-05
CTE,23℃ to 60℃,xflow 1/℃ ISO 11359-2 8.50E-05
HDT/Ae,1.8 MPa Edgew 120*10*4 sp=100mm ISO 75/Ae 100
HDT/Be,0.45MPa Edgew 120*10*4 sp=100mm ISO 75/Be 216
Relative Temp Index,Elec UL 746B 65
Relative Temp Index,Mech w/impact UL 746B 65
Relative Temp Index,Mech w/o impact UL 746B 65
Vicat Softening Temp,Rate B/120 ISO 306 245
PHYSICAL Density g/cm^3 ISO 1183 1.35
Mold Shrinkage on Tensile Bar,flow % E2P Method 1-1.5
Water Absorption,(23℃/sat) % ISO 62 6.5
FLAME CHARACTERISTICS Glow Wire Flammability Index 960℃,passes at mm IEC 60695-2-12 2
Oxygen Index (LOI) % ISO 4589 29
UL Recognized,94V-0  Flame Class Rating mm UL 94 0.75
ELECTRICAL Comparative Tracking Index V IEC 60112 350
Comparative Tracking Index,M V IEC 60112 250
Volume Resistivity Ohm-cm IEC 60093 1.00E+13
PARAMETER Setting Unit
Drying Temperature 75-85
Drying Time 4-6 hrs
Maximum Moisture Content 0.2 %
Mold Temperature 60-90
Rear-Zone 1 Temperature 260-270
Middle-Zone 2 Temperature 270-280
Front-Zone 3 Temperature 270-280
Melt Temperature 270-280