Minlon PA66 10B40HS1 BK061

Minlon® 10B40HS1 BK061 | PA66-MD40 MINERAL REINFORCED NYLON RESIN
 
Regional Availability
North America, South and Central America
 
Processing
Injection Moulding
 
Delivery form
Pellets
 
Additives
Release agent
 
Product Text
Common features of Minlon® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness /toughness, good high temperature performance, good chemical resistance, paintability, dimensional stability and low warpage.
Grades with improved electrical and flammability properties are available within the Zytel® nylon resin product line. In addition, Minlon® nylon resin is available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses.
 
The good melt stability of Minlon® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
 
Minlon® nylon resin typically is used in demanding applications in the automotive, electrical, electronic, domestic appliances and construction industries.
 
Minlon® 10B40HS1 BK061 is a 40% mineral reinforced, heat stabilized, black polyamide 66 resin for injection molding.
 
Injection molding
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80°C
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
 
PROCESSING
Melt temperature optimum = 295°C
Melt temperature range = 285-305°C
Mould temperature optimum = 100°C
Mould temperature range = 70-120°C
Maximum Screw tangential Speed : 0.15 m/s
Flow front speed : 100 mm/s
Hold pressure optimum : 70 MPa
Hold pressure range : 40-100 MPa
Back pressure : low
Hold pressure time : 3 s/mm
Maximum hold-up time : 12 min
 
PROPERTIES
Rheological properties dry / cond Unit Test Standard
Moulding shrinkage,parallel 0.4 / * % ISO 294-4,2577
Moulding shrinkage,normal 0.9 / * % ISO 294-4,2577
Mechanical properties dry / cond Unit Test Standard
Tensile Modulus 10000 / - Mpa ISO 527-1/-2
Stress at break 95 / - Mpa ISO 527-1/-2
Strain at break 2.5 / - % ISO 527-1/-2
Flexural Modulus 9500 / - Mpa ISO 178
Charpy notched impact strength     ISO 179/1eA
23℃ 3 / - kj/㎡
-40℃ 2 / - kj/㎡
lzod notched impact strength     ISO 180/1A
23℃ 3.5 / - kj/㎡
-40℃ 2.5 / - kj/㎡
Thermal properties dry / cond Unit Test Standard
Melting temperature,10℃/min 263 / * ISO 11357-1/-3
Temp. of deflection under load,1.8 MPa 205 / * ISO 75-1/-2
Temp. of deflection under load,0.45 MPa 240 / * ISO 75-1/-2
Coeff. of linear therm. expansion,parallel 36 / * E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion,normal 66 / * E-6/K ISO 11359-1/-2
Flammability dry / cond Unit Test Standard
Burning Behav. at thickness h HB / * class IEC 60695-11-10
Thickness tested 0.7 / * mm IEC 60695-11-10
Other properties dry / cond Unit Test Standard
Density 1510 / - kg/m³ ISO 1183