TORZEN PA66 U4830HSL NC01

添加时间:2013-04-26  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

INVISTA Engineering Polymers
Unreinforced(非增强)


产品:TORZEN™ U4830HSL NC01(BK01) PA66 Resin
描述:TORZEN™ U4830HSL NC01(BK01) 是一个热稳定,润滑注塑级的PA66聚酰胺,颜色有黑色和自然色,PA66 U4830HSL含热稳定剂的设计是为了提高产品保持在高温中应用。
DESCRIPTION:TORZEN™ U4830HSL NC01 is a heat-stabilized, lubricated molding grade PA66 in black color. The heat stabilizer system has been designed to provide excellent property retention in high temperature applications.


Value in use for Pa66:
A unique balance of heat stability, UV resistance, good mechanical properties, fast cycling, and ease of ejection from mold

 

aPPlication sPace:
Automotive, electrical and electronics, appliances, household


targeted and/or Validated Parts:
• Carbon canisters
• Cable ties
• Wiring devices

 

comParatiVe analysis: torZen™ pa66 u4830Hsl resin Vs comPetitiVe grades

测试 单位 TORZEN™ U4830HSL PA66 resin 领先竞争对手的产品
拉伸强度屈服 Mpa 84 83-85
断裂伸长率 % 30 20-40
拉伸模量 MPa 3200 2800-3000
缺口简支梁@23℃ kJ/㎡ 6 5.5-6.6
缺口简支梁@-30℃ kJ/㎡ 4.6 4.5-5.3
HDT @ 0.45 Mpa deg C 199 200
密度 g/cm3 1.14 1.14
可燃性分类 0.71毫米 UL94 V-2 V-2

 

torZen™ u4830Hsl Pa66 resin sHows an excellent balance of ProPerties
torZen u4830Hsl PA66树脂 - UL认可与RTI评级

 

TORZEN™ U4830HSL BK01 PA66 Resin Data

属性   单位 方法
物理 密度 黑:1.14 g/cm3 ISO 1183
成型收缩率,2.0毫米,并行 黑:1.9 % ISO 294-4
成型收缩率,2.0毫米,横向 黑:1.8 % ISO 294-4
水吸收- 24小时 黑:1.4 % ISO 62
水吸收平衡 @ 50%RH   % ISO 62
机械 拉伸屈服强度(50毫米/分钟) 黑:87 本:84 Mpa ISO 527
拉伸断裂强度 - Mpa ISO 527
伸长率 黑:3.9 本:4.2 % ISO 527
断裂伸长率 黑:30 % ISO 527
拉伸模量(1毫米/分钟) 黑:3100 本:3200 Mpa ISO 527
弯曲模量 黑:3100 本:2900 Mpa ISO 178
抗弯强度 黑:101 本:98 Mpa ISO 178
简支梁缺口 在 23℃ 黑:4.6 本:6.0 kJ/㎡ ISO 179
简支梁缺口 在 -30℃ 本:4.6 kJ/㎡ ISO 179
缺口简支梁 在 23℃ NB kJ/㎡ ISO 179
缺口简支梁 在 -30℃ 本:350 kJ/㎡ ISO 179
悬壁梁缺口 在 23℃ 黑:4.7 本:4.8 kJ/㎡ ISO 180
熔点温度,10℃/分钟 黑:263 本:261 ISO 11357
HDT at 0.45 Mpa 黑:203 本:199 ISO 75
HDT at 1.82 Mpa 黑:75 本:64 ISO 75
线性热膨胀系数,2.0毫米,并口,23-55℃   10-4/℃ ASTM E831
线性热膨胀系数,2.0毫米,横向,23-55℃   10-4/℃ ASTM E831
电气 表面电阻率   ohms IEC 60093
体积电阻率,2.0毫米   ohm-cm IEC 60093
介电强度,1.0毫米   kV/mm IEC 60243
对比跟踪指数,3.0毫米   volts IEC 60112
易燃 可燃性等级(0.40毫米) V-2 -- UL 94
灼热丝燃烧指数(0.71毫米)   IEC 60695-2-12
灼热丝燃烧指数(1.5毫米)   IEC 60695-2-12
灼热丝燃烧指数(3.0毫米)   IEC 60695-2-12
灼热丝引燃温度(0.71毫米)   IEC 60695-2-13
灼热丝引燃温度(1.5毫米)   IEC 60695-2-13
灼热丝引燃温度(3.0毫米)   IEC 60695-2-13

 

Product Description
TORZEN™ U4830HSL NC01 is a heat-stabilized, lubricated molding grade PA66 in natural color. The heat stabilizer system has been designed to provide excellent property retention in high temperature applications. U4830HSL is also available in black.


General Information
Material Status
Commercial: Active


Availability
North America, South America, Europe, Asia


Features
Good property retention at elevated temperatures and excellent processability


RoHS
No intentional additives or ingredients used in TORZEN™ U4830HSL NC01 are among those in the European directive 2002/95/EC (RoHs), as amended.

 

成型的工艺

干燥温度               80℃

干燥时间*              3-4小时

料筒温度

后区                      250-270℃

中区                      270-290℃

前区                      270-290℃

喷嘴                      270-290℃

加工(熔体)温度       280-300℃

模具温度               50-90℃

背压**                   2-10巴

排气槽深度            0.007-0.04毫米

垫(范围)                 4-6毫米

建议水份(最大值)    0.18%(重量)

建议的水分(分钟)    0.08%(重量)

螺杆转速                75-180转

 

*初始水分低于0.25%(重量).使用除湿的空气。

**熔体压力

希普能工程塑料