PA66 RX10409D compound 含专有填料

添加时间:2013-03-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP VERTON PA66 RX10409D compound
LNP™ VERTON™ PA66 RX10409D compound
聚酰胺66
专有填料
SABIC Innovative Plastics (Americas)
 
产品说明
Also known as:LNP™ VERTON™ Compound RX10409D
Product reorder name:RX10409D
 
LNP* VERTON* RX10409D is a compound based on Nylon 66 containing proprietary fillers. Added feature of this grade is: Structural.
 
增强填料:含专有填料
定属记号:尼龙66
塑料牌号:PA66 RX10409D
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.simibc.com/sujiao/pa66/LNP/rx10409d.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5 mm/min 2060 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 2.4 % ASTM D 638
Tensile Modulus,5 mm/min 122500 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 3110 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3 mm/min,50 mm span 3070 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 113100 kgf/cm² ASTM D 790
Tensile Stress,break,5 mm/min 199 MPa ISO 527
Tensile Strain,break,5 mm/min 2.3 % ISO 527
Tensile Modulus,1 mm/min 11800 MPa ISO 527
Flexural Stress 285 MPa ISO 178
Flexural Modulus,2 mm/min 10340 MPa ISO 178
IMPACT Value Unit Standard
Charpy Impact,unnotched,23℃ 88 kJ/m² ISO 179/2C
Izod Impact,unnotched,23℃ 119 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 27 cm-kgf/cm ASTM D 256
Multiaxial Impact 71 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 224 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 76 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 24 kJ/m² ISO 180/1A
Charpy Impact,notched,23℃ 22 kJ/m² ISO 179/2C
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2 mm,unannealed 258 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 253 ASTM D 648
CTE,-40℃ to 40℃,flow 2.2E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 6.4E-05 1/℃ ASTM E 831
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 258 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 253 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.42 - ASTM D 792
Density 1.42 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.66 % ASTM D 570
Mold Shrinkage,flow,24 hrs (5) 0.4 % ASTM D 955
Mold Shrinkage,xflow,24 hrs (5) 0.8 % ASTM D 955
Moisture Absorption (23℃/50% RH) 1 % ISO 62
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.