添加时间:2013-03-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP VERTON PA66 RX00327 compound
LNP™ VERTON™ PA66 RX00327 compound
聚酰胺66
专有填料
SABIC Innovative Plastics (Americas)
 
产品说明
Also known as:LNP™ VERTON™ Compound PDX-R-00327
Product reorder name:RX00327
 
LNP* VERTON* RX00327 is a compound based on Nylon 66 resin containing proprietary fillers. Added feature of this material is: Structural.
 
增强填料:含专有填料
定属记号:尼龙66
塑料牌号:PA66 RX00327
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.simibc.com/sujiao/pa66/LNP/rx00327.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5 mm/min 2120 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5 mm/min 2120 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5 mm/min 2 % ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 2 % ASTM D 638
Tensile Modulus,50 mm/min 155400 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 3020 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3 mm/min,50 mm span 3020 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 121300 kgf/cm² ASTM D 790
Tensile Stress,yield,5 mm/min 206 MPa ISO 527
Tensile Stress,break,5 mm/min 206 MPa ISO 527
Tensile Strain,yield,5 mm/min 2 % ISO 527
Tensile Strain,break,5 mm/min 2 % ISO 527
Tensile Modulus,1 mm/min 14740 MPa ISO 527
Flexural Stress 291 MPa ISO 178
Flexural Modulus,2 mm/min 11910 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 111 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 24 cm-kgf/cm ASTM D 256
Multiaxial Impact 50 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 100 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 67 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 27 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2 mm,unannealed 258 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 253 ASTM D 648
CTE,-30℃ to 30℃,flow 3.3E-05 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 7.7E-05 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 257 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 245 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.52 - ASTM D 792
Density 1.52 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.69 % ASTM D 570
Mold Shrinkage,flow,24 hrs (5) 0.2-0.5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs (5) 0.6-0.9 % ASTM D 955
Moisture Absorption (23℃/50% RH) 1 % ISO 62
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.