PA66 RV00CEXS compound 含长玻璃纤维

添加时间:2013-03-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP VERTON PA66 RV00CEXS compound
LNP™ VERTON™ PA66 RV00CEXS compound
聚酰胺66
60%长玻璃纤维
SABIC Innovative Plastics (Americas)
 
产品说明
Also known as:LNP™ VERTON™ Compound RF-700-12 EM
Product reorder name:RV00CEXS
 
LNP* VERTON* RV00CEXS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural.
 
增强填料:含60%长玻璃纤维
材料特点:易于成型
定属记号:尼龙66
塑料牌号:PA66 RV00CEXS
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.simibc.com/sujiao/pa66/LNP/rv00cexs.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5 mm/min 2590 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 1.6 % ASTM D 638
Tensile Modulus,50 mm/min 225100 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 4110 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3 mm/min,50 mm span 4100 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 184500 kgf/cm² ASTM D 790
Tensile Stress,break,5 mm/min 264 MPa ISO 527
Tensile Strain,break,5 mm/min 1.6 % ISO 527
Tensile Modulus,1 mm/min 21860 MPa ISO 527
Flexural Stress 404 MPa ISO 178
Flexural Modulus,2 mm/min 18740 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 119 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 41 cm-kgf/cm ASTM D 256
Multiaxial Impact 98 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 138 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 62 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 37 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2 mm,unannealed 252 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 248 ASTM D 648
CTE,-30℃ to 30℃,flow 4.93E+01 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 6.3E+01 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 253 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 247 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.72 - ASTM D 792
Density 1.72 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.53 % ASTM D 570
Mold Shrinkage,flow,24 hrs (5) 0.3-0.5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs (5) 0.7-0.9 % ASTM D 955
Moisture Absorption (23℃/50% RH) 0.67 % ISO 62
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.