PA66 RV00AE compound 含长玻璃纤维

添加时间:2013-03-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP VERTON PA66 RV00AE compound
LNP™ VERTON™ PA66 RV00AE compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
 
产品说明
LNP* VERTON* RV00AE is a compound based on PA 66 rsin containing Long Glass Fiber. Added features include; Easy Molding.
 
Also known as:LNP™ VERTON™ Compound RF-700-10 EM
Product reorder name:RV00AE
 
增强填料:含长玻璃纤维
材料特点:易于成型
塑料牌号:PA66 RV00AE
定属记号:尼龙66
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.simibc.com/sujiao/pa66/LNP/rv00ae.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,break,5 mm/min 265 MPa ISO 527
Tensile Strain,break,5 mm/min 1.9 % ISO 527
Tensile Modulus,1 mm/min 18380 MPa ISO 527
Flexural Stress,break,2 mm/min 370 MPa ISO 178
Flexural Modulus,2 mm/min 15550 MPa ISO 178
IMPACT Value Unit Standard
Multiaxial Impact 1549 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 89 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 45 kJ/m² ISO 180/1A
Izod Impact,notched 80*10*4 -40℃ 38 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
CTE,23℃ to 60℃,flow 1.86E-05 1/℃ ISO 11359-2
CTE,23℃ to 60℃,xflow 6.73E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 258 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 253 ISO 75/Af
PHYSICAL Value Unit Standard
Mold Shrinkage,flow,24 hrs(5) 0.15-0.35 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 0.22 % ISO 294
Density 1.58 g/cm³ ISO 1183
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.