PA66 RV008E compound 含长玻纤,易成型

添加时间:2013-03-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP VERTON PA66 RV008E compound
LNP™ VERTON™ PA66 RV008E compound
聚酰胺66
40%长玻璃纤维
SABIC Innovative Plastics (Americas)
 
产品说明
Also known as:LNP™ VERTON™ Compound RF-7008 EM
Product reorder name:RV008E
 
LNP* VERTON* RV008E is a compound based on Nylon 66 resin containing 40% Long Glass Fiber. Added features of this material include: Easy Molding, Structural.
 
增强填料:含40%长玻璃纤维
材料特点:易于成型
塑料牌号:PA66 RV008E
定属记号:尼龙66
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.simibc.com/sujiao/pa66/LNP/rv008e.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,break 1750 kgf/cm² ASTM D 638
Tensile Strain,break 1.5 % ASTM D 638
Tensile Modulus,50 mm/min 142700 kgf/cm² ASTM D 638
Flexural Stress 2240 kgf/cm² ASTM D 790
Flexural Modulus 118600 kgf/cm² ASTM D 790
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 54 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 9 cm-kgf/cm ASTM D 256
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 237 ASTM D 648
PHYSICAL Value Unit Standard
Density 1.47 g/cm³ ASTM D 792
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 290-305
Front-Zone 3 Temperature 290-300
Middle-Zone 2 Temperature 290-300
Rear-Zone 1 Temperature 280-295
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.