LNP STAT-KON PA66 RX08408_NA1D004

添加时间:2013-02-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP™ STAT-KON™ Compound PA66 RX08408_NA1D004
 
LNP* Stat-Kon* RX08404_NA1D004 is a compound based on Nylon 66 containing Carbon Powder. Characteristics of this grade include: Electrically Conductive, High Impact.
 
Property
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 460 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 26 % ASTM D 638
Tensile Modulus,50mm/min 19900 kgf/cm² ASTM D 638
Flexural Modulus,1.3mm/min,50mm span 17900 kgf/cm² ASTM D 790
Tensile Stress,break,5mm/min 47 MPa ISO 527
Tensile Strain,break,5mm/min 26 % ISO 527
Tensile Modulus,1mm/min 1930 MPa ISO 527
Flexural Stress 61 MPa ISO 178
Flexural Modulus,2mm/min 1850 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 175 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 14 cm-kgf/cm ASTM D 256
Multiaxial Impact 254 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 224 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 196 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 12 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 195 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 60 ASTM D 648
CTE,-30℃ to 30℃,flow 1.10E-04 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 1.14E-04 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 165 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 117 ISO 75/Af
PHYSICAL Value Unit Standard
Moisture Absorption,50% RH,24 hrs 0.6 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 3-5 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 3-5 % ASTM D 955
Moisture Absorption(23℃/50% RH) 0.87 % ISO 62
ELECTRICAL Value Unit Standard
Volume Resistivity 1.E+03-1.E+06 Ohm-cm ASTM D 257
Surface Resistivity 1.E+03-1.E+06 Ohm ASTM D 257
Source GMD,last updated:2010/09/30
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2010/09/30