LNP STAT-KON PA66 RX05489

添加时间:2013-02-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP™ STAT-KON™ Compound PA66 RX05489

Also known as:LNP™ Stat-kon™ Compound RCFL-4536 Product reorder name:RX05489
LNP* STAT-KON* RX05489 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated.

Property
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,5mm/min 1780 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,5mm/min 1780 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,5mm/min 2.4 % ASTM D 638
Tensile Strain,brk,Type I,5mm/min 2.4 % ASTM D 638
Tensile Modulus,50mm/min 152300 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 2610 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3mm/min,50mm span 2620 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 123300 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 172 MPa ISO 527
Tensile Stress,break,5mm/min 172 MPa ISO 527
Tensile Strain,yield,5mm/min 2.5 % ISO 527
Tensile Strain,break,5mm/min 2.5 % ISO 527
Tensile Modulus,1mm/min 13630 MPa ISO 527
Flexural Stress 258 MPa ISO 178
Flexural Modulus,2mm/min 12040 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 82 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 8 cm-kgf/cm ASTM D 256
Multiaxial Impact 26 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 83 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 48 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 7 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 258 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 246 ASTM D 648
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 255 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 238 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.41 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.62 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0-0 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.7-0.9 % ASTM D 955
Density 1.41 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.92 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 2.E+00-4.E+00 Ohm ASTM D 257
Source GMD,last updated:2009/01/26
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 275-290
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 80-95
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2009/01/26