LNP STAT-KON PA66 REF42

添加时间:2013-02-20  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP™ STAT-KON™ Compound PA66 REF42
 
Also known as:LNP™ Stat-kon™ Compound RCF-1006 Product reorder name:REF42
LNP* Stat-kon* REF42 is a compound based on Nylon 66 resin containing Glass Fiber, Carbon Fiber.
 
Property
 
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,yield 1770 kgf/cm² ASTM D 638
Tensile Stress,break 1770 kgf/cm² ASTM D 638
Tensile Strain,yield 1.8 % ASTM D 638
Tensile Strain,break 1.8 % ASTM D 638
Tensile Modulus,50mm/min 154600 kgf/cm² ASTM D 638
Flexural Stress 2880 kgf/cm² ASTM D 790
Flexural Modulus 112400 kgf/cm² ASTM D 790
Tensile Stress,yield 207 MPa ISO 527
Tensile Stress,break 207 MPa ISO 527
Tensile Strain,yield 2.6 % ISO 527
Tensile Strain,break 2.6 % ISO 527
Tensile Modulus,1mm/min 14360 MPa ISO 527
Flexural Stress 361 MPa ISO 178
Flexural Modulus 17000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 87 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 8 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 53 cm-kgf ASTM D 3763
Multiaxial Impact 27 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 62 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 262 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 253 ASTM D 648
CTE,-40℃ to 40℃,flow 6.66E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 2.16E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 6.60E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 2.10E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 201 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 249 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.35 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.5 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1.1 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.25 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 1.1 % ISO 294
Density 1.35 g/cm³ ISO 1183
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+05-1.E+10 Ohm ASTM D 257
Source GMD,last updated:2008/09/24
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2008/09/24