LNP STAT-KON PA66 RE008

添加时间:2013-02-20  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP™ STAT-KON™ Compound PA66 RE008
 
Also known as:LNP™ Stat-kon™ Compound EMI-X RC-1008 Product reorder name:RE008
LNP* Stat-Kon* RE008 is a compound based on Nylon 66 containing carbon fiber. Characteristics of this grade include: Electrically Conductive.
 
Property
 
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5mm/min 2640 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5mm/min 1.3 % ASTM D 638
Tensile Modulus,5mm/min 339900 kgf/cm² ASTM D 638
Flexural Stress,brk,1.3mm/min,50mm span 3970 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 260900 kgf/cm² ASTM D 790
Tensile Strain,yield,5mm/min 252 % ISO 527
Flexural Modulus,2mm/min 25000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 109 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 11 cm-kgf/cm ASTM D 256
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,1.82 MPa,3.2mm,unannealed 256 ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 255 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.32 - ASTM D 792
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+01-1.E+04 Ohm ASTM D 257
Source GMD,last updated:2012/01/23
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2012/01/23