LNP™ STAT-KON™ Compound PA66 RE0069S
 
Also known as:LNP™ Stat-kon™ Compound RC-1006 FR HS Product reorder name:RE0069S
LNP* STAT-KON* RE0069S is a compound based on Nylon 66 resin containing Flame Retardant, Carbon Fiber. Added features of this material include: Electrically Conductive, Flame Retardant, Heat Stabilized.
 
Property
 
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,yld,Type I,50mm/min 2020 kgf/cm² ASTM D 638
Tensile Stress,brk,Type I,50mm/min 2020 kgf/cm² ASTM D 638
Tensile Strain,yld,Type I,50mm/min 1.6 % ASTM D 638
Tensile Strain,brk,Type I,50mm/min 1.6 % ASTM D 638
Tensile Modulus,50mm/min 274900 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3mm/min,50mm span 2740 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3mm/min,50mm span 2740 kgf/cm² ASTM D 790
Flexural Modulus,1.3mm/min,50mm span 189500 kgf/cm² ASTM D 790
Tensile Stress,yield,5mm/min 207 MPa ISO 527
Tensile Stress,break,5mm/min 207 MPa ISO 527
Tensile Strain,yield,5mm/min 1.4 % ISO 527
Tensile Strain,break,5mm/min 1.4 % ISO 527
Tensile Modulus,1mm/min 24950 MPa ISO 527
Flexural Stress 324 MPa ISO 178
Flexural Modulus,2mm/min 19560 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 103 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 7 cm-kgf/cm ASTM D 256
Multiaxial Impact 25 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 82 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 34 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 8 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 255 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 242 ASTM D 648
CTE,-30℃ to 30℃,flow 8.00E-06 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 8.00E-06 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 255 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 242 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.49 - ASTM D 792
Density 1.5 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.4 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.1-0.3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.7-0.9 % ASTM D 955
Density 1.49 g/cm³ ISO 1183
Moisture Absorption(23℃/50% RH) 0.56 % ISO 62
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+00-4.E+00 Ohm ASTM D 257
Source GMD,last updated:2008/10/09
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2008/10/09