LNP STAT-KON PA66 RE002

添加时间:2013-02-20  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

LNP™ STAT-KON™ Compound PA66 RE002

 
Also known as:LNP™ Stat-kon™ Compound RC-1002 Product reorder name:RE002
LNP* Stat-kon* RE002 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Electrically Conductive.
 
Property
 
TYPICAL PROPERTIES(1)
MECHANICAL Value Unit Standard
Tensile Stress,yield 1370 kgf/cm² ASTM D 638
Tensile Stress,break 1290 kgf/cm² ASTM D 638
Tensile Strain,yield 2.3 % ASTM D 638
Tensile Strain,break 2.3 % ASTM D 638
Tensile Modulus,50mm/min 84300 kgf/cm² ASTM D 638
Flexural Stress 2100 kgf/cm² ASTM D 790
Flexural Modulus 70300 kgf/cm² ASTM D 790
Tensile Stress,yield 131 MPa ISO 527
Tensile Stress,break 131 MPa ISO 527
Tensile Strain,yield 2.1 % ISO 527
Tensile Strain,break 2.1 % ISO 527
Tensile Modulus,1mm/min 7800 MPa ISO 527
Flexural Stress 191 MPa ISO 178
Flexural Modulus 6000 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 37 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 2 cm-kgf/cm ASTM D 256
Instrumented Impact Energy @ peak,23℃ 60 cm-kgf ASTM D 3763
Multiaxial Impact 18 cm-kgf ISO 6603
Izod Impact,unnotched 80*10*4 +23℃ 24 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 3 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2mm,unannealed 258 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 245 ASTM D 648
CTE,-40℃ to 40℃,flow 8.28E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,xflow 2.88E-05 1/℃ ASTM E 831
CTE,-40℃ to 40℃,flow 8.30E-05 1/℃ ISO 11359-2
CTE,-40℃ to 40℃,xflow 2.90E-05 1/℃ ISO 11359-2
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 254 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 241 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.18 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 0.8 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.6-0.8 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 1-3 % ASTM D 955
Mold Shrinkage,flow,24 hrs(5) 0.74 % ISO 294
Mold Shrinkage,xflow,24 hrs(5) 1.3 % ISO 294
Density 1.18 g/cm³ ISO 1183
ELECTRICAL Value Unit Standard
Surface Resistivity 1.E+01-1.E+03 Ohm ASTM D 257
Source GMD,last updated:2008/09/24
Parameter Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 280-305
Front-Zone 3 Temperature 295-305
Middle-Zone 2 Temperature 280-295
Rear-Zone 1 Temperature 265-275
Mold Temperature 95-110
Back Pressure 0.2-0.3 MPa
Screw Speed 30-60 rpm
Source GMD,last updated:2008/09/24