PA66+PA6 84G33 BKB031 含33%玻纤增强,抗冲击

添加时间:2013-11-04  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

Zytel 84G33 BKB031

Zytel® 84G33 BKB031 | (PA66+PA6)-I-GF33 NYLON RESIN
 
Regional Availability
North America, South and Central America
 
Processing
Injection Moulding
 
Delivery form
Pellets
 
Product Text
Common features of Zytel® nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel® nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel® nylon resin, including most flame retardant grades, offer the ability to be coloured.
 
The good melt stability of Zytel® nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
 
Zytel® nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
 
Zytel® 84G33 BKB031 is a 33% glass reinforced toughened polyamide 66 and polyamide 6 co-melt black cube blended resin. This resin was developed for applications requiring strength, stiffness and impact resistance along with good surface appearance.
 
Injection molding
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80℃
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
 
PROCESSING
Melt temperature optimum = 290℃
Melt temperature range = 280-300℃
Mould temperature optimum = 80℃
Mould temperature range = 50-100℃
 
PROPERTIES
Rheological properties dry / cond Unit Test Standard
Rheo Moulding shrinkage,parallel 0.1 / * % ISO 294-4,2577
Moulding shrinkage,normal 0.6 / * % ISO 294-4,2577
Mechanical properties dry / cond Unit Test Standard
Mech Tensile Modulus 9000 / 6929 Mpa ISO 527-1/-2
Stress at break 150 / 115 Mpa ISO 527-1/-2
Strain at break 4 / 8.6 % ISO 527-1/-2
Flexural Modulus 7680 / 5600 Mpa ISO 178
Charpy notched impact strength     ISO 179/1eA
23℃ 21 / 20 kj/㎡
-40℃ 11 / 10 kj/㎡
lzod notched impact strength     ISO 180/1A
23℃ 21 / 23 kj/㎡
-40℃ 15 / 53 kj/㎡
Hardness,Rockwell,M-scale 81 / 53 - ISO 2039-2
Hardness,Rockwell,R-scale 116 / 113 - ISO 2039-2
Thermal properties dry / cond Unit Test Standard
Therm Melting temperature,10℃/min 250 / * ISO 11357-1/-3
Temp. of deflection under load,1.8 MPa 222 / * ISO 75-1/-2
Temp. of deflection under load,0.45 MPa 247 / * ISO 75-1/-2
Coeff. of linear therm. expansion,parallel 15 / * E-6/K ISO 11359-1/-2
Coeff. of linear therm. expansion,normal 120 / * E-6/K ISO 11359-1/-2
Flammability dry / cond Unit Test Standard
Flam Burning Behav. at 1.5 mm nom. thickn. HB / * class IEC 60695-11-10
Thickness tested 1.5 / * mm IEC 60695-11-10
Burning Behav. at thickness h HB / * class IEC 60695-11-10
Thickness tested 0.8 / * mm IEC 60695-11-10
Electrical properties dry / cond Unit Test Standard
Elec Comparative tracking index 600 / - - IEC 60112
Other properties dry / cond Unit Test Standard
Other Density 1340 / - kg/m³ ISO 1183