Ultramid PA6 SEG8 BK-126
Ultramid® PA6 SEG8 BK-126
聚酰胺6
玻璃纤维增强材料,40%
BASF Corporation
 
产品说明
Ultramid SEG8 BK-126 is a 40% glass reinforced, pigmented black, injection molding type 6 nylon requiring high strength, surface aesthetics, and good processability. This product has excellent surface appearance while maintaining a good balance of physical properties, such as high strength, improved toughness, and chemical resistance. It features superior flow properties, and is suited for parts having thinner walls and those requiring long lengths. It shows lower pressure, temperature, and cycle time requirements than conventional grades.
 
Applications
Applications include furniture, but can be used wherever strength and appearance are critical requirements, for example, automotive applications (door handles and mirrors).
 
含添加剂:热稳定剂
填料增强:含40%玻璃纤维增强材料
材料特点:半结晶,尺寸稳定,低粘度,刚性好,高强度,易加工,表面光洁度好,抗热老化,抗蠕变,高流动,耐化学,耐磨蚀,热稳定,韧性好
材料用途:家具,汽车领域的应用,薄壁部件
外观颜色:黑色
产品形式:颗粒料
加工方法:注射成型
塑料牌号:PA6 SEG8 BK-126
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 额定值 单位制 测试方法
密度 1.45 g/cm³ ISO 1183
机械性能 额定值 单位制 测试方法
拉伸应力(断裂,23℃) 160 MPa ISO 527-2
拉伸应变(断裂,23℃) 2.1 % ISO 527-2
弯曲模量(23℃) 10700 MPa ISO 178
冲击性能 额定值 单位制 测试方法
悬壁梁缺口冲击强度(23℃) 12 kJ/m² ISO 180
热性能 额定值 单位制 测试方法
热变形温度(1.8 MPa,未退火) 197 ISO 75-2/A
溶融温度(DSC) 220 ISO 3146
注射 额定值 单位制
干燥温度 83.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.15 %
加工(熔体)温度 270 到 295
模具温度 80.0 到 95.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速  
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.