进口塑胶料
注:请在右边的搜索栏查找产品

PA6 SEG7 含35%玻璃纤维增强

添加时间:2013-09-11  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
Ultramid PA6 SEG7
Ultramid® PA6 SEG7
聚酰胺6
玻璃纤维增强材料,35%
BASF Corporation
 
产品说明
Ultramid SEG7 is a 35% glass reinforced, injection molding type 6 nylon requiring high strength, surface aesthetics, and good processability. This product has excellent surface appearance while maintaining a good balance of physical properties, such as high strength, improved toughness, and chemical resistance. It features superior flow properties, and is suited for parts having thinner walls and those requiring long lengths. It shows lower pressure, temperature, and cycle time requirements than conventional grades.
 
Applications
Applications include power tool, but can be used wherever strength and appearance are critical requirements, for example, automotive applications (door handles and mirrors).
 
黄卡下载:E36632-231203
填料增强:含35%玻璃纤维增强材料
材料特点:刚性佳,高强度,易加工,表面光洁度好,高流动,耐化学,韧性良好,生产阶段快
材料用途:薄壁部件,动力/其它工具,汽车领域的应用
机构评级:ULC Unspecified Rating
外观颜色:自然色
产品形式:颗粒料
加工方法:注射成型
塑料牌号:PA6 SEG7
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 额定值 单位制 测试方法
比重 1.41 g/cm³ ASTM D792,ISO 1183
收缩率 - 流动(3.18 mm) 0.30 %  
吸水率      
24 hr 1.0 % ASTM D570
23℃,24 hr 1.0 % ISO 62
饱和 6.3 % ASTM D570
饱和,23℃ 6.3 % ISO 62
平衡,50% RH 1.7 % ASTM D570
平衡,23℃,50% RH 1.7 % ISO 62
硬度 额定值 单位制 测试方法
洛氏硬度(R 级) 120   ASTM D785
机械性能 额定值 单位制 测试方法
抗张强度(断裂,23℃) 185 MPa ASTM D638,ISO 527-2
伸长率(断裂,23℃) 3.5 % ASTM D638,ISO 527-2
弯曲模量(23℃) 9670 MPa ASTM D790
弯曲强度(23℃) 290 MPa ASTM D790
冲击性能 额定值 单位制 测试方法
悬壁梁缺口冲击强度(23℃) 150 J/m ASTM D256
Drop Impact Resistance(23℃) 3.80 J 内部方法
热性能 额定值 单位制 测试方法
熔融峰值温度 220 ASTM D3418,ISO 3146
RTI Elec     UL 746
0.710 mm 130
1.50 mm 140
3.00 mm 140
RTI Imp     UL 746
0.710 mm 115
1.50 mm 115
3.00 mm 120
RTI     UL 746
0.710 mm 120
1.50 mm 120
3.00 mm 140
可燃性 额定值   测试方法
UL 阻燃等级     UL 94
1.50 mm HB  
3.00 mm HB  
注射 额定值 单位制
干燥温度 83.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.15 %
加工(熔体)温度 270 到 295
模具温度 80.0 到 95.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速  
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.