PA6 BU50I BK-106 高抗冲击,耐低温撞击

添加时间:2013-09-10  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
Ultramid PA6 BU50I BK-106
Ultramid® PA6 BU50I BK-106
聚酰胺6
BASF Corporation
 
产品说明
Ultramid Ultratough Nylon BU50I BK106 is an unreinforced PA6, impact modified injection molding product that maintains its impact strength and ductility to -40 deg F (-40 deg C). The extreme low temperature tolerance of Ultratough Nylon BU50I BK106 makes it ideal for applications in which the weldline impact strength at low temperatures is critical.
 
Ultramid BU50I BK-106 is generally recommended for automotive components, small engines, power tool parts and casings, cold weather and high impact supports gear, such as snowboards, ski components, helmets and hockey masks.
 
UL 黄卡2E36632-231173
含添加剂:冲击调节器
材料特点:超高韧性,改良抗撞击,高抗撞击,可焊接,耐低温,耐低温撞击,延展性
材料用途:Electric Motor Housings,安全帽,动力/其它工具,汽车领域的应用,体育用品
产品形式:颗粒料
加工方法:注射成型
塑料牌号:PA6 BU50I BK-106
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 额定值 单位制 测试方法
比重 1.06 g/cm³ ASTM D792,ISO 1183
收缩率 - 流动(3.18 mm) 1.8 %  
吸水率      
饱和 7.3 % ASTM D570
饱和,23℃ 7.3 % ISO 62
平衡,50% RH 2.1 % ASTM D570
平衡,23℃,50% RH 2.1 % ISO 62
机械性能 额定值 单位制 测试方法
抗张强度      
屈服,23℃ 48.0 MPa ASTM D638
屈服,23℃ 44.0 MPa ISO 527-2
伸长率(断裂,23℃) > 100 % ASTM D638
标称拉伸断裂应变(23℃) > 50 % ISO 527-2
弯曲模量(23℃) 1790 MPa ASTM D790
弯曲强度      
23℃ 67.0 MPa ASTM D790
23℃ 73.0 MPa ISO 178
冲击性能 额定值 单位制 测试方法
悬壁梁缺口冲击强度(23℃) 无断裂   ASTM D256,ISO 180
热性能 额定值 单位制 测试方法
熔融峰值温度 220 ASTM D3418,ISO 3146
注射 额定值 单位制
干燥温度 80.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.15 %
加工(熔体)温度 270 到 300
模具温度 60.0 到 85.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速  
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.