PA6 8233G HS BK-102 含33%玻纤,热稳定

添加时间:2013-08-26  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
Ultramid PA6 8233G HS BK-102
Ultramid® PA6 8233G HS BK-102
聚酰胺6
玻璃纤维增强材料,33%
BASF Corporation
 
产品说明
Ultramid 8233G HS BK-102 is a heat stabilized, black pigmented,33% glass fiber reinforced PA6 injection molding compound. The higher glass fiber reinforcement results in excellent strength, stiffness, high temperature performance and dimensional stability with a high resistance to creep under load. The heat stabilizer system extends properties at elevated temperatures. It offers easy processing and good aesthetics. It maintains its inherent chemical resistance to greases, oils and hydrocarbons. It is suited for metal replacement.
 
Applications
Ultramid 8233G HS BK-102 is generally recommended for applications such as chain saw, power tool housings, weed trimmer components, gears, automotive window hardware, under hood applications including cables, fittings, cooling fans, electrical connectors and coil bobbins.
 
黄卡下载:E36632-231130
含添加剂:热稳定剂
填料增强:含33%玻璃纤维增强材料
材料特点:耐碳氢化合物,尺寸稳定,低粘度,刚性高,高强度,可加工性良好,表面光洁度佳,抗热老化,抗蠕变,流动性好,耐化学,耐磨蚀,热稳定
材料用途:草坪和园林设备,齿轮,电线电缆应用,动力/其它工具,金属取代,连接器,配件,汽车的发动机罩下的零件,汽车领域的应用,外壳,线轴
外观颜色:黑色
外观形式:颗粒料
加工方法:注射成型
塑料牌号:PA6 8233G HS BK-102
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 干燥 调节后的 单位制 测试方法
比重 1.39 -- g/cm3 ASTM D792,ISO 1183
收缩率 - 流动(3.18 mm) 0.30 -- %
吸水率
24 hr 1.1 -- % ASTM D570
23℃,24 hr 1.1 -- % ISO 62
饱和 6.4 -- % ASTM D570
饱和,23℃ 6.4 -- % ISO 62
平衡,50% RH 1.8 -- % ASTM D570
平衡,23℃,50% RH 1.8 -- % ISO 62
硬度 干燥 调节后的 单位制 测试方法
洛氏硬度(R 级) 121 -- ASTM D785
机械性能 干燥 调节后的 单位制 测试方法
拉伸模量 ISO 527-2
-40℃ 10300 -- MPa
23℃ 10200 5600 MPa
80℃ 4820 -- MPa
121℃ 4010 -- MPa
抗张强度
断裂,-40℃ 230 215 MPa ASTM D638
断裂,23℃ 180 99.0 MPa ASTM D638
断裂,80℃ 90.0 70.0 MPa ASTM D638
断裂,121℃ 70.0 60.0 MPa ASTM D638
断裂,-40℃ 230 -- MPa ISO 527-2
断裂,23℃ 170 99.0 MPa ISO 527-2
断裂,80℃ 90.0 -- MPa ISO 527-2
断裂,121℃ 70.0 -- MPa ISO 527-2
伸长率
断裂,-40℃ 3.0 2.5 % ASTM D638
断裂,23℃ 3.5 7.0 % ASTM D638
断裂,80℃ 7.0 6.5 % ASTM D638
断裂,121℃ 7.0 6.5 % ASTM D638
断裂,23℃ 3.0 7.0 % ISO 527-2
弯曲模量
23℃ 8990 -- MPa ASTM D790
23℃ 8500 5200 MPa ISO 178
弯曲强度
23℃ 280 -- MPa ASTM D790
23℃ 245 130 MPa ISO 178
冲击性能 干燥 调节后的 单位制 测试方法
简支梁缺口冲击强度 ISO 179
-30℃ 10 -- kJ/m2
23℃ 10 -- kJ/m2
简支梁无缺口冲击强度(23℃) 65 -- kJ/m2 ISO 179
悬壁梁缺口冲击强度(23℃) 110 -- J/m ASTM D256
Drop Impact Resistance(23℃) 4.07 -- J 内部方法
热性能 干燥 调节后的 单位制 测试方法
载荷下热变形温度
0.45 MPa,未退火 218 -- ASTM D648
0.45 MPa,未退火 215 -- ISO 75-2/B
1.8 MPa,未退火 208 -- ASTM D648
1.8 MPa,未退火 205 -- ISO 75-2/A
熔融峰值温度 220 -- ASTM D3418,ISO 3146
线形热膨胀系数 - 流动 3.8E-5 -- cm/cm/℃ ASTM E831
RTI Elec UL 746
0.710 mm 130 --
1.50 mm 140 --
3.00 mm 140 --
RTI Imp UL 746
0.710 mm 115 --
1.50 mm 115 --
3.00 mm 120 --
RTI UL 746
0.710 mm 130 --
1.50 mm 140 --
3.00 mm 140 --
可燃性 干燥 调节后的 测试方法
UL 阻燃等级 UL 94
0.600 mm HB --
1.50 mm HB --
3.00 mm HB --
注射 干燥 单位制
干燥温度 83.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.15 %
加工(熔体)温度 270 到 295
模具温度 80.0 到 95.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.