Ultramid PA6 8231G HS
Ultramid® PA6 8231G HS
聚酰胺6
玻璃纤维增强材料,14%
BASF Corporation
 
产品说明
Ultramid 8231G HS is a heat stabilized, 14% glass fiber reinforced PA6 injection molding compound. It is also available in non-heat stabilized (Ultramid 8231) and/or pigmented versions. The glass fiber reinforcement enhances performance such as strength, stiffness and heat deflection temperature. The heat stabilizer system extends the properties at elevated temperatures. It also has excellent chemical resistance to greases, oils and hydrocarbons.
 
Applications
Ultramid 8231G HS is ideally suited for more demanding performance applications such as safety helmet parts, washers, gears, engine and motor parts, chutes, and higher temperature environments.
 
黄卡下载:E36632-231123
含添加剂:热稳定剂
填料增强:含14%玻璃纤维增强材料
材料特点:半结晶,尺寸稳定,低粘度,刚性好,高强度,光泽高,抗弯曲,可加工性好,表面光洁度佳,抗热老化,流动性好,耐化学,耐磨蚀,热稳定
材料用途:安全帽,草坪和园林设备,齿轮,动力/其它工具,高温应用,连接器,汽车领域的应用,汽车外部零件
外观颜色:可用颜色,自然色
外观形式:颗粒料
加工方法:注射成型
塑料牌号:PA6 8231G HS
定属记号:尼龙6
代理销售:苏州希普能工程塑料 185 5121 3137 谭经理
 
物料数据
物理性能 干燥 调节后的 单位制 测试方法
比重 1.23 -- g/cm3 ASTM D792,ISO 1183
收缩率 - 流动(3.18 mm) 0.50 -- %
吸水率
24 hr 1.4 -- % ASTM D570
23℃,24 hr 1.4 -- % ISO 62
饱和 8.1 -- % ASTM D570
饱和,23℃ 8.1 -- % ISO 62
平衡,50% RH 2.3 -- % ASTM D570
平衡,23℃,50% RH 2.3 -- % ISO 62
硬度 干燥 调节后的 单位制 测试方法
洛氏硬度(R 级) 121 -- ASTM D785
机械性能 干燥 调节后的 单位制 测试方法
拉伸模量 ISO 527-2
-40℃ 5950 6600 MPa
23℃ 5960 2640 MPa
80℃ 2470 2300 MPa
121℃ 2090 1900 MPa
抗张强度
断裂,-40℃ 160 170 MPa ASTM D638,ISO 527-2
断裂,23℃ 140 79.0 MPa ASTM D638
断裂,80℃ 60.0 20.0 MPa ASTM D638,ISO 527-2
断裂,121℃ 50.0 40.0 MPa ASTM D638,ISO 527-2
断裂,23℃ 140 80.0 MPa ISO 527-2
伸长率
断裂,-40℃ 3.0 4.0 % ASTM D638
断裂,23℃ 4.0 9.0 % ASTM D638,ISO 527-2
断裂,80℃ 8.0 15 % ASTM D638
断裂,121℃ 7.0 6.0 % ASTM D638
弯曲模量
-40℃ 5860 6430 MPa ASTM D790
23℃ 5310 2400 MPa ASTM D790
65℃ 2400 -- MPa ASTM D790
121℃ 1930 -- MPa ASTM D790
23℃ 4770 2210 MPa ISO 178
弯曲强度
-40℃ 214 219 MPa ASTM D790
23℃ 172 101 MPa ASTM D790
65℃ 110 -- MPa ASTM D790
90℃ 90.0 -- MPa ASTM D790
121℃ 76.0 -- MPa ASTM D790
23℃ 160 65.0 MPa ISO 178
冲击性能 干燥 调节后的 单位制 测试方法
简支梁缺口冲击强度 ISO 179
-30℃ 5.5 -- kJ/m2
23℃ 6.5 -- kJ/m2
简支梁无缺口冲击强度(23℃) 40 -- kJ/m2 ISO 179
悬壁梁缺口冲击强度
23℃ 59 -- J/m ASTM D256
23℃ 5.0 -- kJ/m2 ISO 180
热性能 干燥 调节后的 单位制 测试方法
热变形温度
0.45 MPa,未退火 217 -- ISO 75-2/B
1.8 MPa,未退火 200 -- ASTM D648
1.8 MPa,未退火 195 -- ISO 75-2/A
熔融峰值温度 220 -- ASTM D3418,ISO 3146
线形热膨胀系数
流动 5.0E-5 -- cm/cm/℃ ASTM E831
流动 3.9E-5 -- cm/cm/℃
横向 7.8E-5 -- cm/cm/℃
RTI Elec UL 746
0.800 mm 130 --
1.50 mm 130 --
3.00 mm 130 --
6.00 mm 130 --
RTI Imp UL 746
0.800 mm 95.0 --
1.50 mm 105 --
3.00 mm 105 --
6.00 mm 105 --
RTI UL 746
0.800 mm 105 --
1.50 mm 105 --
3.00 mm 105 --
6.00 mm 105 --
电气性能 干燥 调节后的 单位制 测试方法
体积电阻率
1.50 mm > 1.0E+13 -- ohms·cm ASTM D257
-- > 1.0E+13 -- ohms·cm IEC 60093
介电强度 40 -- kV/mm IEC 60243-1
介电常数 IEC 60250
100 Hz 3.60 --
1 MHz 3.40 --
耗散因数 IEC 60250
100 Hz 0.010 --
1 MHz 0.020 --
可燃性 干燥 调节后的 单位制 测试方法
UL 阻燃等级 UL 94
0.800 mm HB --
1.50 mm HB --
3.00 mm HB --
6.00 mm V-2 --
注射 干燥 单位制
干燥温度 80.0
干燥时间 2.0 到 4.0 hr
建议的最大水分含量 0.15 %
加工(熔体)温度 250 到 290
模具温度 80.0 到 95.0
注塑压力 3.50 到 12.5 MPa
注射速度 快速
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.