Celstran PA6 PA6-GF50-01

添加时间:2013-04-30  信息来源:http://www.simibc.com/  作者:苏州希普能塑料

CELSTRAN® PA6-GF50-01 AD3002 BLACK
CELSTRAN® PA6-GF50-01 AF3001 NATURAL
CELSTRAN® PA6-GF50-01 AS3011 RED

 

CELSTRAN PA6-GF50-01 | PA6 | Glass Reinforced

 

Description
50% long strand fiber glass reinforced nylon 6 Natural

 

Other Processing 
Injection Molding
Celstran can be processed on a standard injection molding unit. A general purpose metering screw is recommended with a zone distribution of 40% feed, 40% transition, and 20% metering. A free flowing check ring assembly is recommended.

 

Melt Temp:285-295℃.
Mold Temp:85-95℃.


ISO Data Physical properties Value Unit Test Standard
Phys Density 1560 kg/m³ ISO 1183
Mech Tensile modulus (1mm/min) 16000 MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 245 MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 2.02 % ISO 527-2/1A
Flexural modulus (23℃) 14700 MPa ISO 178
Flexural strength (23℃) 390 MPa ISO 178
Charpy notched impact strength @ 23℃ 39 kJ/m² ISO 179/1eA
Therm DTUL @ 1.8 MPa 215 ISO 75-1/-2

Processing
Pre Drying

 

Necessary low maximum residual moisture content: 0.18%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Note: Material can be over dried and may discolor.

 

Drying time (h):2 - 4
Drying temperature (℃):70 - 80