Celstran PA6 PA6-GF30-01

添加时间:2013-04-30  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
CELSTRAN® PA6-GF30-01 AD3002 BLACK
CELSTRAN® PA6-GF30-01 AF3001 NATURAL
 
CELSTRAN PA6-GF30-01 | PA6 | Glass Reinforced
 
30% long strand glass fiber reinforced nylon 6 Black
 
Injection Molding
Celstran can be processed on a standard injection molding unit.A general purpose metering screw is recommended with a zone distribution of 40% feed, 40% transition, and 20% metering. A free flowing check ring assembly is recommended.
 
Melt Temp:270-280℃.
Mold Temp:85-95℃.
 
ISO Data Physical properties Value Unit Test Standard
Phys Density 1360  kg/m3 ISO 1183
Mech Tensile modulus (1mm/min) 9510  MPa ISO 527-2/1A
Tensile stress at break (5mm/min) 155  MPa ISO 527-2/1A
Tensile strain at break (5mm/min) 1.78  % ISO 527-2/1A
Flexural modulus (23℃) 8830  MPa ISO 178
Charpy notched impact strength @ 23℃ 18  kJ/m2 ISO 179/1eA
Therm DTUL @ 1.8 MPa 207 ISO 75-1/-2

 

 

Processing

Pre Drying

 

Necessary low maximum residual moisture content: 0.18%

 

CELSTRAN PA should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< -30℃. The time between drying and processing should be as short as possible.

 

Note: Material can be over dried and may discolor.

 

Drying time (h):2-4

Drying temperature (℃):70-80