LNP VERTON PA6 PX91200 compound
LNP™ VERTON™ PA6 PX91200 compound
聚酰胺6
专有填料
SABIC Innovative Plastics (Americas)
 
产品说明
LNP VERTON* PX91200 is a compound based on Nylon 6 resin containing Proprietary Fillers. Added features of this material include: High Impact, Structural
 
Also known as:LNP™ VERTON™ Compound PDX-P-91200
Product reorder name:PX91200
 
增强填料:含专有填料
材料特点:高冲击
塑料牌号:PA6 PX91200
定属记号:尼龙6
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.simibc.com/sujiao/pa6/LNP/px91200.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,break 181 MPa ISO 527
Tensile Strain,break 2 % ISO 527
Tensile Modulus,1 mm/min 12100 MPa ISO 527
Flexural Stress 250 MPa ISO 178
Flexural Modulus 10290 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched 80*10*4 +23℃ 68 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 25 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 225 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 222 ISO 75/Af
PHYSICAL Value Unit Standard
Density 1.49 g/cm³ ISO 1183
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 265-275
Front-Zone 3 Temperature 275-290
Middle-Zone 2 Temperature 265-275
Rear-Zone 1 Temperature 250-260
Mold Temperature 80-95
Back Pressure 0.3-0.7 MPa
Screw Speed 30-60 rpm
PA6 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6 is among the most-used engineering materials, with excellent impact strength, moldability and paintability, fair heat resistance, and good wear and friction characteristics.