PA6 PX06418 compound 含专有填料,热稳定

添加时间:2013-03-22  信息来源:http://www.simibc.com/  作者:苏州希普能塑料
LNP VERTON PA6 PX06418 compound
LNP™ VERTON™ PA6 PX06418 compound
聚酰胺6
专有填料
SABIC Innovative Plastics (Americas)
 
产品说明
LNP* VERTON* PX06418 is a compound based on Nylon 6 containing proprietary fillers. Added features of this grade are: Heat Stabilized, Structural.
 
Also known as:LNP™ VERTON™ Compound PDX-P-00700 HS
Product reorder name:PX06418
 
增强填料:含专有填料
材料特点:热稳定
塑料牌号:PA6 PX06418
定属记号:尼龙6
加工方法:注射成型
销售电话:185 5121 3137 谭经理
湘樟专卖:http://www.simibc.com/sujiao/pa6/LNP/px06418.html
 
材料物性
MECHANICAL Value Unit Standard
Tensile Stress,brk,Type I,5 mm/min 2060 kgf/cm² ASTM D 638
Tensile Strain,brk,Type I,5 mm/min 2.5 % ASTM D 638
Tensile Modulus,50 mm/min 121900 kgf/cm² ASTM D 638
Flexural Stress,yld,1.3 mm/min,50 mm span 3150 kgf/cm² ASTM D 790
Flexural Stress,brk,1.3 mm/min,50 mm span 3130 kgf/cm² ASTM D 790
Flexural Modulus,1.3 mm/min,50 mm span 101900 kgf/cm² ASTM D 790
Tensile Stress,yield,5 mm/min 193 MPa ISO 527
Tensile Stress,break,5 mm/min 182 MPa ISO 527
Tensile Strain,break,5 mm/min 2.6 % ISO 527
Tensile Modulus,1 mm/min 10900 MPa ISO 527
Flexural Stress 290 MPa ISO 178
Flexural Modulus,2 mm/min 9530 MPa ISO 178
IMPACT Value Unit Standard
Izod Impact,unnotched,23℃ 106 cm-kgf/cm ASTM D 4812
Izod Impact,notched,23℃ 28 cm-kgf/cm ASTM D 256
Multiaxial Impact 53 cm-kgf ISO 6603
Instrumented Impact Total Energy,23℃ 156 cm-kgf ASTM D 3763
Izod Impact,unnotched 80*10*4 +23℃ 64 kJ/m² ISO 180/1U
Izod Impact,notched 80*10*4 +23℃ 27 kJ/m² ISO 180/1A
THERMAL Value Unit Standard
HDT,0.45 MPa,3.2 mm,unannealed 213 ASTM D 648
HDT,1.82 MPa,3.2mm,unannealed 208 ASTM D 648
CTE,-30℃ to 30℃,flow 4.77E+01 1/℃ ASTM D 696
CTE,-30℃ to 30℃,xflow 1.14E+02 1/℃ ASTM D 696
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm 213 ISO 75/Bf
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm 207 ISO 75/Af
PHYSICAL Value Unit Standard
Specific Gravity 1.41 - ASTM D 792
Density 1.4 g/cm³ ASTM D 792
Moisture Absorption,50% RH,24 hrs 1.1 % ASTM D 570
Mold Shrinkage,flow,24 hrs(5) 0.1-0.3 % ASTM D 955
Mold Shrinkage,xflow,24 hrs(5) 0.4-0.6 % ASTM D 955
Moisture Absorption(23℃/50% RH) 1.7 % ISO 62
Injection Molding Value Unit
Drying Temperature 80
Drying Time 4 hrs
Maximum Moisture Content 0.15-0.25 %
Melt Temperature 265-275
Front-Zone 3 Temperature 275-290
Middle-Zone 2 Temperature 265-275
Rear-Zone 1 Temperature 250-260
Mold Temperature 80-95
Back Pressure 0.3-0.7 MPa
Screw Speed 30-60 rpm
PA6 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6 is among the most-used engineering materials, with excellent impact strength, moldability and paintability, fair heat resistance, and good wear and friction characteristics.